- Polypropylene Copolymer
Polypropylene Copolymer (PPCP) is a colorless, non flammable, non reactive solid with no odor. See Product Description. Polypropylene Copolymer (PPCP) is usually stored and/or transported as 25 Kg Bags or 1 MT FIBC jumbo Bags. It is used in raw material for plastic Processing industry.
Grade Data Sheet
Halene – P
TECHNICAL DATA SHEET M312 Polypropylene Impact Co-polymer
Characteristics
M312 is a Heterophasic Polypropylene Impact Co-polymer (PPiCP), produced by the latest
generation Spheripol II Technology. This PPiCP is primarily suitable for Injection Molding process. M312 combines excellent process ability with high Flow, low Cycle Time, good Impact – Stiffness balance and good Gloss.
Application
• Automotive Components
• Housewares, Thermowares & Sanitary-wares
• Industrial Components
• Luggage
• Paint Pail
• Compounding
| Property | Test Method | Unit | Value |
| Melt Flow Index (2.16 kg & 2300 C) | ASTM D 1238 | g/10 min | 12 |
| Density at 23°C | ASTM D 1505 | g/cm3 | 0.9 |
| Tensile Strength at Yield (50 mm/min) | ASTM D 638 | MPa | 22 |
| Tensile Elongation at Yield (50 mm/min) | (Type I – with Extensometer) | % | 7 |
| Flexural Modulus | ASTM D 790A | MPa | 1000 |
| Notched Izod Impact Strength (23°C) | ASTM D 256A | J/m | 120 |
| Vicat Softening Point (10N) | ASTM D 1525 | 0C | 145 |
| Heat Deflection Temperature (0.455 MPa) | ASTM D 648 | 0C | 88 |
| Typical Processing Temperature | |||
| Barrel Temperature | 0C | 160-250 | |
| Mold Temperature | 0C | 30-40 | |
Mechanical properties are tested on Injection Molded Test Specimens prepared as per ASTM D 4101.
The information & data presented herein are typical values and should not be construed as specification. No warranty or guarantee expressed or implied is made regarding performance. The information & data are subject to change without prior intimation based
on research & development work undertaken by the company.
Polypropylene Impact Copolymer Injection Molding
Product Description:
PP Impact Copolymer 3120MA is a heterophasic natural colored high impact resistance & antistatic agent containing grade produced by the latest Spheripol- II Technology with following features:
- Good process ability.
- Good balance of Impact & Stiffness properties
- Reduced static charge build – up in product
Recommended Applications:
PP Impact Copolymer 3120MA is recommended for
Injection Molding & Compounding applications like
- Industrial & Automotive components
- Appliances & Housewares
- Furniture
- Compounding
Typical Properties:
| Property | Test Method | UOM | Value |
| Melt Flow Index (2300C & 2.16 Kg) | ASTM D 1238 | gm/10 min | 12 |
| Density @ 23oC | ASTM D 1505 | gm/cm3 | 0.9 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | ASTM D 638 | MPa | 27 |
| Elongation @ Yield (50 mm/min) | ASTM D 638 | % | 8 |
| Flexural Modulus (1.3 mm/min) | ASTM D 790 | MPa | 1100 |
| Notched Izod Impact Strength @ 23oC | ASTM D 256 | J/m | 80 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/mm 2 ) | ASTM D 648 | oC | 105 |
| Vicat Softening Point (10 N) | ASTM D 1525 | oC | 150 |
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Recommended Processing Temperature: 170 – 230 oC
Packaging Information:
This material is packed and available in raffia bags with net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS, however, customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause spillage and wastage. IOCL does not warranty loss of material due to poor material handling practices.
Regulatory Information:
PP Co-polymer 3120MA shall meet the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Co-polymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water’. Additives incorporated in this grade shall meet the positive list of constituents as prescribed in IS 10909. The Grade and the additives incorporated in it will also comply with the FDA: CFR Title 21,177.1520, Olefin Polymers.
Storage & Handling:
Prevent PP Material from direct exposure to sunlight & heat to avoid quality deterioration. The storage location should be dry, dust free and the Storage
temperature should not exceed 50 oC. Non – compliance to these precautionary
measures can lead to degradation of the product causing Color changes, Odor &
inadequate product performance. It is advised to process PP material within 06 months after delivery.
Polypropylene Impact Copolymer Injection Molding
Product Description:
PP Impact Block Copolymer 3030MG is a heterophasic natural colored high impact resistance grade produced by the latest Spheripol II Technology with following features:
• Medium flow for easy processing.
• High Impact Strength.
• High Stiffness
Recommended Applications:
PP Impact Copolymer 3030MG is recommended for Injection Molded applications like
• Automotive components
• Appliances
• Industrial components
• Caps & Closures
Typical Properties:
| Tested Properties | Test Method | UOM | Value |
| Melt Flow Index (2300C & 2.16 Kg) | ASTM D 1238 | gm/10 min | 3.5 |
| Density @ 23oC | ASTM D 1505 | gm/cm3 | 0.9 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | ASTM D 638 | MPa | 27 |
| Elongation @ Yield (50 mm/min) | ASTM D 638 | % | 9 |
| Flexural Modulus (1.3 mm/min) | ASTM D 790 | MPa | 1100 |
| Notched Izod Impact Strength @ 23oC | ASTM D 256 | J/m | >150 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/mm 2 ) | ASTM D 648 | oC | 88 |
| Vicat Softening Point (10 N) | ASTM D 1525 | oC | 150 |
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Recommended Processing Temperature: 170 – 230 oC
Packaging Information:
This material is packed and available in raffia bags with net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS, however, customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause spillage and wastage. IOCL does not warranty loss of material due to poor material handling practices.
Regulatory Information:
PP Copolymer 3030MG shall meet the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Copolymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water’. The grade and Additives incorporated in this grade shall meet the positive list of constituents as prescribed in IS 10909. The Grade and the additives incorporated in it will also comply with
the FDA: CFR Title 21,177.1520, Olefin Polymers.
Storage & Handling:
Prevent PP Material from direct exposure to sunlight & heat to avoid quality deterioration. The storage location should be dry, dust free and the Storage
temperature should not exceed 50 oC. Non – compliance to these precautionary
measures can lead to degradation of the product causing Color changes, Odor &
inadequate product performance. It is advised to process PP material within 06 months after delivery.
CO 15EG
IMPACT COPOLYMER
FOR EXTRUSION AND BLOW MOULDED PRODUCTS
Repo! CO I 5EG is recommended for use in Blow Moulding and Extrusion processes where high impact strength is required. It is an ideal material to use in making blow moulded containers, sheets, thermoforming, automotive trims etc.
Typical Characteristics
| Property | Test Method | Unit | Typical Value* |
| Melt Flow Rate (230″C/2.16 kg) | ASTM D 1238 | el0 min | 1.8 |
| Tensile Strength at Yield (50 mm/min) | ASTM D638 | M Pa | 27 |
| Elongation at Yield (50 mmimin) | ASTM D638 | % | I I |
| Flexural Modulus (1% secant) | ASTM D790A | M Pa | 1000 |
| Notched lzod Impact Strength (23’C) | ASTM D256 | Jim | 200 |
| Heat Deflection Temperature (455 kPa) | ASTM D648 | ‘C | 95 |
* Typical values, not to be taken as specification. Al the mechanical properties as per ASTM D638 Type I specimen injection moulded in accordance with /.STN1 D4 0
Applications
Sheets, blow moulded containers
Regulatory Information
- Meets the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Copolymers for safe use in contact with foodstuff, pharmaceuticals, and drinking water’. Additives incorporated in this grade conform to the positive list of constituents as prescribed in IS 10909. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21,177.1520, Olefin polymers
Storage Recommendations
- Bags should be stored in dry /closed conditions at temperatures below 50°C and protected from UV/direct sunlight