- PP FILM
Polysure F10SR is Polypropylene Homo-polymer, produced by Latest Novolen Technology & Primarily suitable for Tubular water quench film applications. F10SR combines exceptional process ability with superior Slip, Anti Blocking properties, Excellent Clarity and Gloss.
Grade Data Sheets
F10SR Polypropylene Homo-polymer TQPP Films
Product Characteristics:
Polysure F10SR is Polypropylene Homo-polymer, produced by Latest Novolen Technology & Primarily suitable for Tubular water quench film applications. F10SR combines exceptional process ability with superior Slip, Anti Blocking properties, Excellent Clarity and Gloss.
Recommended Applications:
F10SR is recommended to Process Tubular Quenched (TQ) Film for packaging foodstuffs and garments, snack food, grocery & general purpose packaging.
Typical Properties:
| Properties | Test Method | Units | Values* |
| Melt Flow Index ( 230oC & 2.16 kg) | ASTM D1238 | g/10 min | 10.5 |
| Tensile Strength @ Yield (50mm / min) | ASTM D638 | MPa | 34 |
| Tensile Elongation @ Yield (50mm / min) | ASTM D638 | % | 9 |
| Flexural Modulus | ASTM D790 | MPa | 1500 |
| Notch Izod Impact Strength ( 23oC) | ASTM D256 | J/m | 30 |
| Vicat Softening Point (10N) | ASTM D1525 | oC | 154 |
| Heat Deflection Temperature (0.455 MPa) | ASTM D648 | oC | 95 |
*All the mechanical properties as per ASTM D638 Type I Injection molded specimen prepared in accordance with ASTM D 4101
Processing Guidelines:
Barrel Temperature : 180 – 230°C
Die-temperature : 190 – 210°C
Storage & Handling:
Bags should be stored in dry & dust free environment at temperature below 50 oC and Prevent from direct exposure to sunlight & heat to avoid quality deterioration.
Regulatory Requirements:
F10SR is manufactured complying the requirements specified in IS 10910 on “Specification for Polypropylene & its Co-polymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water”. Furthermore the Additives added in this grade formulation compiles to the “Positive list of constituents of Polypropylene and its Copolymers in contact with Foodstuff, Pharmaceutical & Drinking water’ as laid down under IS 10909. In general the additives & constituents used in the grade are in line with requirement laid down under FDA: CFR Title 21,177.1520, Olefin Polymers.
Disclaimer: The information & data presented herein are typical values & should not be considered as specification and may be used as guideline only. HMEL does not undertake any
responsibility for any outcome or results from the adoption or replication of the above mentioned data & information there on for possible use for various applications. HMEL reserves the
right to change the information & data without any prior notice or information. The user will solely be responsible for any process/product usage.
HPCL-Mittal Energy Limited (HMEL), INOX Tower, Plot No.17, Sector-16A, Noida – 201301 (U.P), India. Tel: 0120-4634500. Corporate Site: www.hmel.in
Polypropylene Homopolymer TQPP Film
PP Homopolymer 1100FS is a natural colored grade produced by the latest Spheripol II Technology with following features:
• Excellent Processability,
• Excellent clarity & gloss.
• Contains Slip & Antiblock additives.
Recommended Applications:
PP Homopolymer 1100FS is recommended for Production of Tubular Water Quenched Polypropylene blown film (TQPP films) for packaging of
• Textile Over wraps
• Snack & bakery foods
• Garment bags
Typical Properties:
| Tested Properties | Test Method | UOM | Values* |
| Resin Properties | |||
| Melt Flow Index (2300C & 2.16 Kg) | ASTM D 1238 | gm/10 min | 11.0 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | ASTM D 638 | MPa | 35.0 |
| Elongation @ Yield (50 mm/min) | ASTM D 638 | % | 10.0 |
| Flexural Modulus (1.3 mm/min) | ASTM D 790 | MPa | 1500 |
| Notched Izod Impact Strength @ 23oC | ASTM D 256 | J/m | 21 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/m2) | ASTM D 648 | oC | 100 |
| Vicat Softening Point (10 N) | ASTM D 1525 | oC | 151 |
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Recommended Processing Temperature: 170 – 220 oC
Packaging Information:
This material is packed and available in raffia bags with a net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS, however, the customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause spillage and wastage. IOCL does not warranty the loss of material due to poor material handling practices.
Regulatory Information:
PP Homopolymer 1100FS shall meet the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Copolymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water’. The grade and Additives incorporated in this grade shall meet the positive list of constituents as prescribed in IS 10909. The Grade and the additives incorporated in it will also comply with the FDA: CFR Title 21,177.1520, Olefin Polymers.
Storage & Handling:
Prevent PP Material from direct exposure to sunlight & heat to avoid quality deterioration. The storage location should be dry, dust-free and the Storage temperature should not exceed 50 oC. Non – compliance with these precautionary measures can lead to degradation of the product causing Color changes, Odor & inadequate product performance. It is advised to process PP material within 06 months after delivery.
Polypropylene Homo polymer
Product Description:
PP Homo-polymer 1350YG is a natural colored grade produced by the latest Spheripol II
Technology with following features:
- High melt flow and specified for high speed
production of fine denier fiber / Non-woven. - Excellent Process ability
Recommended Applications:
PP Homo-polymer 1350YG is recommended for Production of :
- Spun bonded non-woven fabrics
- Fine denier Multi-filament yarns.
Typical Properties:
| Tested Properties | Test Method | UOM | Values* |
| Resin Properties | |||
| Melt Flow Index (2300C & 2.16 Kg) | ASTM D 1238 | gm/10 min | 35.0 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | ASTM D 638 | MPa | 36.0 |
| Elongation @ Yield (50 mm/min) | ASTM D 638 | % | 11.0 |
| Flexural Modulus (1.3 mm/min) | ASTM D 790 | MPa | 1200 |
| Notched Izod Impact Strength @ 23oC | ASTM D 256 | J/m | 20 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/mm 2) | ASTM D 648 | oC | 85 |
| Vicat Softening Point (10 N) | ASTM D 1525 | oC | 150 |
* Typical characteristics of the product given purely as a guide. Film properties were measured on 25.4 microns blown film extruded at a blow-up ratio (BUR)
2.5.
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Recommended Processing Temperature: 170 – 230 oC
Packaging Information:
This material is packed and available in raffia bags with net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS, however, customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause spillage and wastage. IOCL does not warranty loss of material due to poor material handling practices.
Regulatory Information:
PP Homo-polymer 1350YG shall meet the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Co-polymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water’. The grade and Additives incorporated in this grade shall meet the positive list of constituents as prescribed in IS 10909. The Grade and the additives incorporated in it will also comply with the FDA: CFR Title 21,177.1520, Olefin Polymers.
Storage & Handling:
Prevent PP Material from direct exposure to sunlight & heat to avoid quality deterioration. The storage location should be dry, dust free and the Storage temperature should not exceed 50 oC. Non – compliance to these precautionary measures can lead to degradation of the product causing Color changes, Odor & inadequate product performance. It is advised to process PP material within 06 months after delivery.
Disclaimer: IOCL assumes no liability whatsoever in respect of application, processing or any use made of the aforementioned information or products, or any consequence thereof. No liability whatsoever shall attached to any of the IOCL companies for any infringement of the rights owned or controlled by a third party in intellectual, industrial or other property by reason of application, processing or use of the afore-mentioned information or products by the user.
Polypropylene Homopolymer Woven Sacks
Product Description:
PP Homopolymer 1030RG is a natural colored grade produced by the latest Spheripol II Technology with the following features:
- Exceptional processability
- Low water carryover
- Good balance of tenacity & elongation
Recommended Applications:
PP Homopolymer 1030RG is recommended for stretched tapes of Woven sacks like
- Fabrics for general packaging
- Cement, Polymers & Fertilizers packaging
- Foodgrains packaging
- FIBC for bulk industrial packaging
- Carpet backing
Typical Properties:
| Tested Properties | Test Method | UOM | Values* |
| Resin Properties | |||
| Melt Flow Index (2300C & 2.16 Kg) | ASTM D 1238 | gm/10 min | 3.3 |
| Density @ 23oC | ASTM D 1505 | gm/cm3 | 0.90 |
| Mechanical Properties | |||
| Tensile Strength @ Yield (50 mm/min) | ASTM D 638 | MPa | 35 |
| Elongation @ Yield (50 mm/min) | ASTM D 638 | % | 12 |
| Flexural Modulus (1.3 mm/min) | ASTM D 790 | MPa | 1550 |
| Notched Izod Impact Strength @ 23 oC | ASTM D 256 | J/m | 50 |
| Thermal Properties | |||
| Heat Deflection Temperature (0.46 N/m2) | ASTM D 648 | oC | 95 |
| Vicat Softening Point (10 N) | ASTM D 1525 | oC | 156 |
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
Recommended Processing Temperature: 170 – 230 oC
Packaging Information:
This material is packed and available in raffia bags with a net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS, however, the customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause spillage and wastage. IOCL does not warranty the loss of material due to poor material handling practices.
Regulatory Information:
PP Homopolymer 1030RG shall meet the requirements stipulated in IS 10910 on ‘Specification for Polypropylene and its Copolymers for safe use in contact with Foodstuff, Pharmaceutical & Drinking water’. The grade and Additives incorporated in this grade shall meet the positive list of constituents as prescribed in IS 10909. The Grade and the additives incorporated in it will also comply with the FDA: CFR Title 21,177.1520, Olefin Polymers
Storage & Handling:
Prevent PP Material from direct exposure to sunlight & heat to avoid quality deterioration. The storage location should be dry, dust-free and the Storage temperature should not exceed 50 oC. Non – compliance with these precautionary measures can lead to degradation of the product causing Color changes, Odor & inadequate product performance. It is advised to process PP material within 06 months after delivery.