LD FILM

Porto

- LD FILM

RELIANCE LD FS040

24FSO40 LOW DENSITY POLYETHYLENE

FOR GENERAL PURPOSE FILM APPLICATIONS

24FSO40 is a film grade Low Density Polyethylene (LDPE) produced by high pressure tubular process. It can be extruded with considerable ease on any conventional LDPE extruder. The polymer has been blended with necessary additives during manufacture to obtain good surface slip and easy openability between two layers of the film.

Typical Characteristics*
Property Test Method Unit Typical Value**
Melt Flow Index ( I 90°C/2. I 6 kg) ASTM D 1238 gm/1 0 min 4.0
Density (23°C) ASTM D 1505 gm/cm’ 0.922
Tensile Strength at Break (MD/TD) ASTM D882 M Pa 18/16
Elongation at Break (MD/TD) ASTM D882 % 250/400
Dart Impact Strength (F-50) ASTM D 1709/A gilim 2.0

 

*Typical Characteristics and not to be taken as specifications

** Typical Values (Mechanical) with 40p film made with I mm die gap & 2.0 BUR

Applications

High slip grade for shopping bags, general purpose packaging. Regulatory Information

  • Meets the requirements stipulated in standard IS : 10146 on “Specification for Polyethylene for safe use in contact with foodstuffs, pharmaceuticals, and drinking water”. It also conforms to the positive list of constituents as prescribed in IS : 10141. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21, I 77.1520, Olefin polymers.

Storage Recommendations

  • Bags should be stored in dry/ closed conditions at temperatures below 50°C and protected from UV/ direct sunlight.

RELIANCE 1005

I 005FY20 LOW DENSITY POLYETHYLENE

FOR LIQUID PACKAGING APPLICATIONS

1005FY20 is a film grade Low-Density Polyethylene (LDPE). It has been specially formulated for the production of films for liquid milk packaging on fully automatic form, fill and seal type of machines. Film produced from this grade exhibits good impact resistance and heat-sealing characteristics. The incorporation of necessary additives in the polymer ensures good surface slip and smooth flow of film on packaging machines. It can be pigmented by using suitable food contact approved masterbatches.

Typical Characteristics*

Property Test Method Unit Typical Value**
Melt Flow Index (190°C/2.16 kg) ASTM D 1238 gm/I 0 min 0.5
Density (23°C) ASTM D 1505 gm/cm’ 0.920
Tensile Strength at Break (MD/TD) ASTM D882 MPa 21/20
Elongation at Break (MD/TD) ASTM D882 % 300/525
Dart Drop Impact (F-50) ASTM D I 709/A griiim 3.7

 

*Typical Characteristics and not to be taken as specifications

** Typical Values (Mechanical) with 40 p film made with I mm die gap & 2.0 BUR

Applications

Medium slip grade for mono & co-extruded film for liquid packaging. Regulatory Information

  • Meets the requirements stipulated in standard IS : 10146 on “Specification for Polyethylene for safe use in contact with foodstuffs, pharmaceuticals, and drinking water”. It also conforms to the positive list of constituents as prescribed in IS : 10141. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21, I 77.1520, Olefin polymers.

Storage Recommendations

  • Bags should be stored in dry/ closed conditions at temperatures below 50°C and protected from UV/ direct sunlight.

RELIANCE 1020

LOW-DENSITY POLYETHYLENE

1020FA20  FILM GRADE

1020FA20 is a film grade and can be processed easily on conventional blown film lines. The grade is manufactured without any slip additive to facilitate adhesion during lamination.

TYPICAL CHARACTERISTICS*

PROPERTY TEST METHOD UNIT TYPICAL VALUE**
Density (23OC) ASTM D 792 g/cc 0.920
Melt Flow Index (190O C / 2.16 Kg) ASTM D 1238 g/10 min. 2.0
Tensile Strength at Break (MD / TD) ASTM D 882 MPa 20.0 / 19.0
Elongation at Break (MD / TD) ASTM D 882 % 275 / 425
Dart Impact Strength (F50) ASTM D 1709/A g / µm 3.0

 

* Typical characteristics and not to be taken as specifications

** Typical value (Mechanical) with 40 µ film made with 0.7 mm die gap & 2.5 BUR

APPLICATIONS:

Adhesive lamination film / Foam film

Regulatory Information

  • Meets the requirement stipulated in standard IS: 10146 on “Specification for Polyethylene for safe use in contact with foodstuff, pharmaceutical, and drinking water”. It also conforms to the positive list of constituents as prescribed in IS: 10141. The grade and the additives incorporated in it also comply with the FDA:CFR Title 21,177,1520, Olefin polymers

Storage Recommendations

  • Bags should be stored in dry/closed conditions at temperatures below 50°C and protected from UV / direct sunlight.

RELIANCE 16MA400

Reliance POLYMERS
16MA400 LOW-DENSITY POLYETHYLENE

FOR INJECTION MOULDING & MASTERBATCH RESIN

16MA400 is an injection moulding grade Low-Density Polyethylene (LDPE) produced by the high-pressure tubular process. The high melt flow index makes it ideal for molding very thin, intricate, and large items having adequate mechanical properties. This grade is also an ideal choice for making masterbatches with higher loading.

Typical Characteristics

Property Test Method Unit Typical Value••
Melt Flow Index (I 90°C/2. I 6 kg) ASTM D 1238 gm/1 0 min 30
Density (23°C) ASTM D 1505 gm/cm3 0.918
Tensile Strength atYield ASTM D638 MPa 10
Elongation at yield ASTM D638 % 40
Flexural Modulus ASTM D790 MPa I40
Notched Izod Impact Strength ASTM D256 Jim No Break
Vicat Softening Point ASTM D 1525 °C 84

 

*Typical Characteristics and not to be taken as specifications
**Mechanical Properties are on Injection Moulded Specimen

Applications

Masterbatches, powder coating, soft moldings. Regulatory Information

  • Meets the requirements stipulated in standard IS: 10146 on “Specification for Polyethylene for safe use in contact with foodstuffs, pharmaceuticals, and drinking water”. It also conforms to the positive list of constituents as prescribed in IS : 10141. The grade and the additives incorporated in it also comply with the FDA: CFR Title 21,177.1520, Olefin polymers.

Storage Recommendations

  • Bags should be stored in dry/ closed conditions at temperatures below 50°C and protected from UV/ direct sunlight.